| Material | Density (×1000 kg/m3) |
Melting Point (ºC) |
Boiling Point (ºC) |
Thermal Conductivity W/m °C |
Heat Capacity J/Kg °C |
Thermal Expansion Coefficient microns/m °C |
| Acrylic | 14 | 0.14 | ||||
| Air [STP] | .001293 | 660.3 | 2519 | 1006 | ||
| Aluminum [Al] | 2.71 | 660.3 | 2519 | |||
| Aluminum [2024-T3] | 2.77 | 190.4 | 963 | 22.68 | ||
| Aluminum [6061-T6] | 2.77 | 155.8 | 963 | 24.3 | ||
| Aluminum [7079-T6] | 2.74 | - | 121.1 | 963 | 24.3 | |
| Ammonia - liquid | 0.6821 | 660.3 | 2519 | - | ||
| Beryllium QMV | 1.850 | - | 147.1 | 1884 | 24.66 | |
| Brass | 8.4 - 8.75 | 930.0 | - | |||
| Brass; Naval | 8.4 | - | - | |||
| Brass; Red (80% Cu, 20% Zn) | 8.75 | 1000 | - | |||
| Brass; Yellow (65% Cu, 35% Zn) | 8.47 | 930? | 116 | 377 | 20.3 | |
| Brick | 1.8 - 2.4 | - | - | |||
| Bronze; Regular | 7.8 - 8.8 | 1050 | - | |||
| Bronze; Manganese | 8.3 | - | - | |||
| Carbon [C] | 2.25 | 4492 | 3642 | |||
| Ceramic | 2 - 3 | 3870 | - | |||
| Concrete | 2.3 - 2.4 | - | - | 1.8 | ||
| Copper [Cu] | 8.9 | 1085 | 2562 | 392.9 | 385 | 16.56 |
| Copper Alloy | 8.23 | 925.0 | - | |||
| Cork | 0.15 - 0.2 | - | - | |||
| Glass | 2.4 - 2.8 | - | - | |||
| Glass, Borosilicate | 2.230 | - | - | 1.13 | ||
| Gold [Au] | 19.32 | 1064 | 2856 | 297.7 | 130 | 4.39 |
| Iron [Fe] | 7.87 | 1538 | 2861 | 83.5 | 440 | |
| Iron (Cast) | 7 - 7.4 | - | - | |||
| Iron (Wrought) | 7.4 - 7.8 | - | - | |||
| Lead [Pb] | 11.3 | 327.5 | 1749 | 37.04 | 130 | 52.74 |
| Magnesium [Mg] | 1.74 | 650.0 | 1090 | |||
| Magnesium HK31A-H24 | 1.79 | (1246?) | (2061?) | 114.2 | 544 | 25.2 |
| Magnesium AZ31B-H24 | 1.77 | 1246 | 2061 | 95.19 | 1047 | 26.1 |
| Monel (67% Ni, 30% Cu) | 8.84 | 1330 | - | |||
| Nickel [Ni] | 8.89 | 1455 | 2913 | 91.73 | 461 | 12.96 |
| Nylon; Polyamide | 1.1 | - | - | 0.24 | ||
| Platinum [Pt] | 21.4 | 1768 | 3825 | 69.23 | 130 | 9 |
| Rubber | 0.96 - 1.3 | - | - | |||
| Silicon [Si] | 2.33 | 1382 | - | |||
| Silver [Ag] | 10.49 | 961.8 | 2162 | 417.1 | 235 | 19.8 |
| Solder; Tin-Lead | 8.17 - 11.34 | 215.0 | - | |||
| Steel AISI 304 | 8.030 | - | 16.27 | 503 | 17.82 | |
| Steel AISI 1020 | 7.85 | 1425 | - | 46.73 | 419 | 11.34 |
| Stone; Granite | 2.6 | - | - | |||
| Stone; Limestone | 2 - 2.9 | - | - | |||
| Stone; Marble | 2.6 - 2.9 | - | - | |||
| Stone; Quartz | 2.6 | - | - | ~1.32 | ||
| Tin [Sn] | 7.3 | 231.9 | 2602 | |||
| Titanium [Ti] | 4.54 | 1668 | 3287 | |||
| Titanium Alloy | 4.51 | - | - | |||
| Tungsten [W] | 19.3 | 3422 | 5555 | 164.4 | 138 | 4.5 |
| Water (4°C) | 0.9997 | 0 | 100 | 603 | 4216 | |
| Wood; Ash | 0.56 - 0.64 | - | - | |||
| Wood; Douglas Fir | 0.48 - 0.56 | - | - | |||
| Wood; Oak | >0.64 - 0.72 | - | - | |||
| Wood; Southern Pine | 0.55 - 0.64 | - | - | 0.11 | ||
| Zinc [Zn] | 7.14 | 419.5 | 907.0 |